Catalytic purification of tertiary butyl alcohol

ABSTRACT

Motor-fuel grade tertiary butyl alcohol which is prepared, for example, by reacting propylene with tertiary butyl hydroperoxide to form propylene oxide and a tertiary butyl alcohol reaction product contaminated with residual amounts of tertiary butyl hydroperoxide and ditertiary butyl peroxide can be effectively catalytically treated under mild conversion conditions including a temperature of about 80° to 280° C. with an unsupported catalyst composed of nickel, copper, chromia and iron, or the oxides thereof, or a catalyst containing nickel, copper, chromia and iron which is supported on silica in order to substantially selectively convert the two peroxide contaminants to tertiary butyl alcohol and to thereby provide a treated tertiary butyl alcohol product substantially free from contaminating quantities of such peroxides.

BACKGROUND OF THE INVENTION

1. Field of the Invention

This invention relates to the catalytic purification of tertiary butyl alcohol prepared by the reaction of propylene with tertiary butyl hydroperoxide. More particularly, this invention relates to a method for the removal of residual contaminating quantities of tertiary butyl hydroperoxide and ditertiary butyl peroxide from a tertiary butyl alcohol feedstock which is prepared by the reaction of propylene with tertiary butyl hydroperoxide and is useful as an octane-enhancing component for motor fuels. In accordance with the present invention the peroxide-contaminated feedstock is brought into contact with a catalyst which is either an unsupported nickel, copper, chromia, iron oxide catalyst or a nickel, copper, chromia, iron oxide catalyst supported on silica in order to substantially selectively reduce both the tertiary butyl hydroperoxide and the ditertiary butyl peroxide to tertiary butyl alcohol.

2. Prior Art

a. Process

A process for the manufacture of substituted epoxides from alpha olefins such as propylene is disclosed in Kollar U.S. Pat. No. 3,351,653 which teaches that an organic epoxide compound can be made by reacting an olefinically unsaturated compound with an organic hydroperoxide in the presence of a molybdenum, tungsten, titanium, columbium, tantalum, rhenium, selenium, chromium, zirconium, tellurium or uranium catalyst. When the olefin is propylene and the hydroperoxide is tertiary butyl hydroperoxide, propylene oxide and tertiary butyl alcohol are coproducts. U.S. Pat. No. 3,350,422 teaches a similar process using a soluble vanadium catalyst. Molybdenum is the preferred catalyst. A substantial excess of olefin relative to the hydroperoxide is taught as the normal procedure for the reaction. See also U.S. Pat. No. 3,526,645 which teaches the slow addition of organic hydroperoxide to an excess of olefin as preferred.

Stein, et al. in U.S. Pat. No. 3,849,451 have improved upon the Kollar process of U.S. Pat. Nos. 3,350,422 and 3,351,635 by requiring a close control of the reaction temperature, between 90°-200° C. and autogeneous pressures, among other parameters. Stein et al. also suggests the use of several reaction vessels with a somewhat higher temperature in the last vessel to ensure more complete reaction. The primary benefits are stated to be improved yields and reduced side reactions.

It is known that isobutane can be oxidized with molecular oxygen to form a corresponding tertiary butyl hydroperoxide and that the oxidation reaction can be promoted, for example with an oxidation catalyst (see Johnston U.S. Pat. No. 3,825,605 and Worrell U.S. Pat. No. 4,296,263.

Thus, tertiary butyl alcohol can be prepared either by the direct thermal or catalytic reduction of tertiary butyl hydroperoxide to tertiary butyl alcohol or by the catalytic reaction of propylene with tertiary butyl hydroperoxide to provide propylene oxide and tertiary butyl alcohol.

It is also known that tertiary butyl alcohol can be used as an octane-enhancing component when added to a motor fuel, such as gasoline. Thus, it has heretofore been proposed, as shown, for example, by Grane U.S. Pat. No. 3,474,151 to thermally decompose tertiary butyl hydroperoxide and ditertiary butyl peroxide to form tertiary butyl alcohol. The thermal decomposition must be conducted with care, as pointed out by Grane, in that tertiary butyl alcohol will start to dehydrate at a temperature of about 450° F. and in that the dehydration becomes rapid at temperatures above about 475° F. Moreover, the product from the thermal decomposition normally contains a minor amount of tertiary butyl hydroperoxide and ditertiary butyl peroxide which have an adverse effect upon the quality of motor fuels and must be substantially completely removed if the tertiary butyl alcohol is to be fully effective. Grane proposes to accomplish this thermally by heating tertiary butyl alcohol containing small quantities of such peroxides at a temperature of 375°-475° F. for a period of 1 to 10 minutes.

This concept was expanded upon by Grane et al. in U.S. Pat. Nos. 4,294,999 and 4,296,262 to provide integrated processes wherein, starting with isobutane, motor-fuel grade tertiary butyl alcohol was prepared by the oxidation of isobutane (e.g., in the presence of a solubilized molybdenum catalyst) to produce a mixture of tertiary butyl alcohol and tertiary butyl hydroperoxide from which a fraction rich in tertiary butyl hydroperoxide could be recovered by distillation. This stream, after being debutanized was subjected to thermal decomposition under pressure at a temperature of less than 300° F. for several hours to significantly reduce the concentration of the tertiary butyl hydroperoxide. However, the product of this thermal decomposition step still contained residual tertiary butyl hydroperoxide, most of which was thereafter removed by a final thermal treatment of the contaminated tertiary butyl hydroperoxide in the manner taught by Grane U.S. Pat. No. 3,474,151.

Thus, the removal of trace quantities of tertiary butyl hydroperoxide from motor grade tertiary butyl alcohol has received appreciable attention. However, little appears to have been published concerning the removal of trace quantities of ditertiary butyl peroxide, the more refractory of the two peroxides. This may be explainable both because ditertiary butyl peroxide is not always present in trace quantities in motor grade tertiary butyl alcohol (its presence or absence being a function of the reaction conditions used in oxidizing the isobutane starting material) and because, when present, it is present in significantly lower amounts. For example, after decomposition of the major amount of tertiary butyl hydroperoxide formed by the oxidation of isobutane, the tertiary butyl hydroperoxide residual content will normally be about 0.1 to about 1 wt. %, based on the tertiary butyl alcohol, while the residual ditertiary butyl peroxide content, if any, will only be about 0.1 to 0.5 wt. %.

Sanderson et al. U.S. Pat. No. 4,547,598 discloses the use of unsupported cobalt borate and cobalt borate supported on titanium dioxide to decompose organic hydroperoxides to alcohols. It has also been proposed to remove the residual hydroperoxide contaminants from tertiary butyl alcohol through the use of a heterogeneous cobalt oxide catalyst containing a copper oxide promoter as shown, for example, by Coile U.S. Pat. No. 4,059,598. Allison et al. in U.S. Pat. No. 3,505,360 have more generically taught that alkenyl hydroperoxides can be decomposed catalytically through the use of a catalyst based on a metal or compound of a metal of group IV-A, V-A or VI-A.

Other prior art patents relating to the production of hydroperoxides, but not with the problem of residual tertiary hydroperoxide contamination and tertiary butyl alcohol include patents such as Rust U.S. Pat. No. 2,383,919; Harvey U.S. Pat. No. 3,449,217; Poenisch et al. U.S. Pat. No. 3,778,382 and Williams et al. U.S. Pat. No. 3,816,548.

In West German DE No.3248465-A a two-step process is disclosed wherein isobutane is oxidized noncatalytically with air to a conversion of about 48-90% to form the corresponding hydroperoxide, which is then catalytically decomposed under hydrogenation conditions in the presence of a supported catalyst such as palladium, platinum, copper, rhenium, ruthenium or nickel to form tertiary butyl alcohol. The decomposition product obtained using 1.3% palladium on lithium spinel as a catalyst contained significant quantities of acetone, water and methanol.

Mabuchi et al. U.S. Pat. No. 4,112,004 discloses a process for preparing monohydric or polyhydric alcohols from organic peroxides in the presence of a nickel catalyst by continuously feeding a solution of the organic peroxide (e.g., butadiene peroxide) and a suspension of the nickel catalyst to a reactor in a controlled ratio and continuously withdrawing reaction mixture at a rate adequate to maintain a constant weight and composition of the reaction mixture in the reactor.

In U.S. Pat. No. 4,123,616 to Mabuchi et al. a process is disclosed for hydrogenating an organic peroxide to the corresponding mono- or polyhydric alcohol in a suspension or fluidized bed process under hydrogen pressure in the presence of a nickel catalyst. Examples are given showing the conversion of butadiene peroxide to 1,4-butane diol and 1,2-butane diol and the conversion of tertiary butyl hydroperoxide to tertiary butyl alcohol.

b. Catalysts

Godfrey U.S. Pat. No. 3,037,025 discloses the preparation of N-alkyl substituted piperazines using catalyst compositions consisting of the metals and oxides of copper, nickel and cobalt (including mixtures thereof) which may also be promoted by the inclusion of a normally non-reducible metal oxide such as chromium, aluminum, iron, calcium, magnesium, manganese and the rare earths. Preferred catalyst compositions are indicated as containing from about 44 to about 74 wt. % of nickel, about 5 to about 55 wt. % of copper and about 1 to about 5 wt. % of chromia.

Moss U.S. Pat. No. 3,151,112 discloses catalyst compositions useful for the preparation of morpholines including one or more metals from the group including copper, nickel, cobalt, chromium, molybdenum, manganese, platinum, palladium and rhodium, which may also be promoted with normally nonreducible oxides such as chromium oxide, molybdenum oxide and manganese oxide. Representative catalyst compositions include those containing from about 60 to about 85 wt. % of nickel, about 14 to about 37 wt. % of copper and about 1 to about 5 wt. % of chromia. Nickel, copper, chromia catalysts are also disclosed in Moss U.S. Pat. No. 3,151,115 and Moss U.S. Pat. No. 3,152,998.

Winderl et al. U.S. Pat. No. 3,270,059 teaches the use of catalysts containing a metal of groups I-B and VIII of the Periodic System. Examples of suitable catalysts are stated to be copper, silver, iron, nickel, and particularly, cobalt.

Boettger et al. U.S. Pat. No. 4,014,933 discloses catalysts containing cobalt and nickel promoted with copper such as those containing from about 70 to about 95 wt. % of a mixture of cobalt and nickel and from about 5 to about 30 wt. % of copper.

Habermann U.S. Pat. No. 4,152,353 discloses catalyst compositions comprising nickel, copper and a third component which may be iron, zinc, zirconium or a mixture thereof such as catalysts containing from about 20 to about 49 wt. % of nickel, about 36 to about 79 wt. % of copper and about 1 to about 15 wt. % of iron, zinc, zirconium or a mixture thereof. Similar catalyst compositions are mentioned in Habermann U.S. Pat. No. 4,153,581.

European patent application No. 0017651 filed Oct. 20, 1980, contains a disclosure of catalyst compositions related to those disclosed by Habermann, such catalyst compositions being composed of nickel or cobalt, copper and iron, and zinc or zirconium such as compositions containing 20 to 90% cobalt, 3 to 72% copper and 1 to 16% of iron, zinc or zirconium and catalyst compositions containing 20 to 49% nickel, 36 to 79% copper and 1 to 16% of iron, zinc or zirconium.

German Offen. No. 2,721,033 discloses a catalyst composition containing 35% nickel, about 87.5% iron and a minor amount of chromia.

Johansson et al. U.S. Pat. No. 3,766,184 discloses catalyst compositions composed of iron and nickel and/or cobalt.

SUMMARY OF INVENTION

The feedstocks of the present invention comprise tertiary butyl alcohol contaminated with tertiary butyl hydroperoxide and ditertiary butyl peroxide.

When isobutane is treated to form tertiary butyl hydroperoxide, the reaction product will normally contain some tertiary butyl alcohol and other oxygenated by-products such as ditertiary butyl peroxide, acetone, etc., as well as unreacted isobutane. After the unreacted isobutane is flashed, a fraction composed mostly of tertiary butyl alcohol may be recovered as a distillate fraction in order to further concentrate the desired tertiary butyl hydroperoxide reaction product. The tertiary butyl alcohol distillate, which will normally be contaminated with tertiary butyl hydroperoxide, ditertiary butyl peroxide, etc., may be used as a feedstock for the process of the present invention.

Tertiary butyl alcohol is suitably reacted with propylene by a process of the type disclosed in Kollar U.S. Pat. No. 3,351,635 to provide an initial reaction product composed mostly of unreacted propylene, propylene oxide and tertiary butyl alcohol. However, residual qua ntities of tertiary butyl hydroperoxide and ditertiary butyl peroxide and other oxygenated impurities are normally present and remain dissolved in the tertiary butyl alcohol recovered from the reaction mixture. This tertiary butyl alcohol product can also be used as a feedstock for the process of the present invention.

Tertiary butyl hydroperoxide can decompose thermally and/or catalytically to form acetone. Tertiary butyl alcohol can be decomposed to form water and isobutylene. Accordingly, the tertiary butyl alcohol, as initially recovered is not entirely satisfactory for use as an octane-enhancing component for motor fuels, such as gasoline. Thus, tertiary butyl alcohol will normally be considered unsatisfactory for motor fuel use if it contains more than about 3 wt. % of acetone, more than about 1 wt. % of isobutylene, more than about 100 ppm of ditertiary butyl peroxide and more than 100 ppm of tertiary butyl hydroperoxide. Desirably, the tertiary butyl alcohol will contain about 1 wt. % or less of acetone, 0.5 wt. % or less of isobutylene and 10 ppm or less of ditertiary butyl peroxide and 100 ppm or less of tertiary butyl hydroperoxide.

It has been surprisingly discovered in accordance with the present invention that motor-fuel grade tertiary butyl alcohol which is contaminated with residual amounts of ditertiary butyl peroxide and tertiary butyl hydroperoxide can be effectively catalytically treated with an unsupported catalyst compound of nickel, copper, chromia, iron oxide or a nickel, copper, chromia, iron oxide catalyst supported on silica under mild catalytic conditions including a temperature of about 80° to 220° C. at a pressure sufficient to maintain a liquid phase reaction mixture (normally, about 200 to 800 psig., depending on reaction temperature. Higher pressures of up to about 2000 psig. can be used, if desired, but there is no particular advantage in using the higher pressures. This treatment will substantially selectively convert the peroxide contaminants to tertiary butyl alcohol and thereby provide a treated product substantially free of contaminating quantites of tertiary butyl hydroperoxide and ditertiary butyl peroxide. Thus, the formation of unwanted oxygenated derivatives of the peroxide contaminates, including acetone, methanol and isobutylene is substantially avoided.

The results obtained with the process of the present invention are surprising and unexpected in several respects. Catalytic or thermal decomposition of tertiary butyl hydroperoxide and ditertiary butyl peroxide normally results in the formation of acetone as the favored decomposition product. Thus, the favorable effect on the quality of motor fuel grade tertiary butyl alcohol that is obtained by the substantially complete elimination of the two peroxides will be largely counterbalanced if the decomposition product is principally acetone or if more than trace amounts of isobutylene are present.

Moreover, we have found that catalysts that are effective for the substantially complete decomposition of tertiary butyl hydroperoxide are normally only partially effective, at best, for the catalytic reduction of ditertiary butyl peroxide. We have also found that the "inert" supports that are normally suggested for use with heavy metal catalysts can, and do, exert an unexpected influence on the course of the reactions involved in the catalytic reduction of ditertiary butyl peroxide. We were surprised to discover that silica could be used as a support.

Thus, the provision of the process of the present invention wherein a motor-fuel grade tertiary butyl alcohol feedstock containing contaminating quantities of both ditertiary butyl peroxide and tertiary butyl hydroperoxide, is catalytically treated for the reduction of the peroxides so that they are substantially completely removed without significantly adding to the level of contamination due to the formation of acetone, methanol and isobutylene constitutes a distinct advantage over the prior art.

STARTING MATERIALS

The starting materials for the process of the present invention include a motor-fuel grade tertiary butyl alcohol feedstock obtained in the manner described above by the reaction of propylene with tertiary butyl hydroperoxide to form propylene oxide and tertiary butyl alcohol by the oxidation of isobutane to form tertiary butyl hydroperoxide, etc.

The motor-fuel grade tertiary butyl alcohol feedstock obtained by the reaction of propylene with tertiary butyl hydroperoxide to form propylene oxide and tertiary butyl alcohol will contain contaminating quantities of teritary butyl hydroperoxide, ditertiary butyl peroxide, and acetone, and may also contain contaminating quantities of methanol and isobutylene. The normal levels of contamination of such materials are such that the tertiary butyl alcohol will normally contain, prior to treatment, from about 0.1 to about 5 wt. % of tertiary butyl hydroperoxide and from about 0.1 to about 5 wt. % of ditertiary butyl peroxide. Minor quantities of other contaminants may also be present.

As indicated earlier, the reaction conditions used in the catalytic oxidation of isobutane will sometimes result in the formation of ditertiary butyl peroxide. Thus, the feedstock to be used for the practice of the present invention is an impure motor grade tertiary butyl alcohol containing from about 0.1 to about 5 wt. % of tertiary butyl hydroperoxide and from about 0.1 to about 5 wt. % of ditertiary butyl peroxide.

The catalyst compositions of the present invention consist essentially of the oxides of and/or metallic nickel, copper, chromia and iron in the proportions (on an oxygen-free basis) of about 1 to about 20 wt. % of iron, about 1 to about 6 wt. % of chromia and with the balance being nickel and copper in the weight ratio of about 2 to 3 parts of nickel per part of copper. For example, the catalyst compositions of the present invention may consist essentially of about 30 to about 60 wt. % of nickel, about 5 to about 40 wt. % of copper, about 0.5 to about 10 wt. % of chromia and about 1 to about 30 wt. % of iron, with the nickel and copper being proportioned as indicated above.

More preferably, the catalyst compositions of the present invention will contain about 1 to about 20 wt. % of iron and about 1 to about 5 wt. % of chromia, with the nickel and copper being proportioned as indicated above.

As indicated, the catalyst compositions of the present invention may be composed of one or more of the oxides of nickel, copper, chromium and iron in the proportions (calculated on an oxygen-free basis) given above. When an oxide catalyst is prepared, it will tend to be reduced to the metallic form during use.

The catalyst may also be supported on a suitable silica support such as Kieselguhr.

Although the catalyst compositions of the present invention may be utilized in powdered form in conducting batch reactions, their utility is enhanced when they are used in pelleted form for catalyzing the reaction in a continuous process. When a catalyst is used in pelleted form for a continuous reaction, it is necessary that the pellets have good physical and chemical properties so that they will not disintegrate or break during the course of the continuous peroxide reduction. The catalyst compositions of the present invention have such properties.

Catalytic Treatment of Tertiary Butyl Alcohol

In accordance with the present invention, a tertiary butyl alcohol feedstock, as above described, is brought into contact with a catalyst of the present invention under reaction conditions correlated to substantially selectively catalytically convert both the tertiary butyl hydroperoxide and ditertiary butyl peroxide contaminants in the tertiary butyl alcohol feedstock to tertiary butyl alcohol with not more than a minor increase in the level of contamination of the acetone, methanol and isobutylene also normally present in the tertiary butyl alcohol as contaminants.

The reaction may be conducted batchwise in an autoclave using powdered catalyst or may be conducted on a continuous basis by passing the tertiary butyl alcohol through a reactor containing a bed of a catalyst of the present invention under reaction conditions including a temperature within the range of about 80° to about 280° C. and, more preferably, from about 110 to about 180° C. The reaction is preferably conducted at 200 to 800 psig., although higher pressures of up to about 2000 psig. may be used if desired. When the reaction is conducted batchwise, contact time may suitably be from about 0.5 to about 4 hours. When the reaction is conducted on a continuous basis, the tertiary butyl alcohol should be passed over the bed of catalyst at a liquid hourly space velocity of about 0.25 to about 5.

The reaction product, after being degassed, is suitable for use as an octane-enhancing component of motor fuel, such as gasoline.

Thus, for example, the effluent from the reactor may be passed through a phase separation zone in order to permit gaseous reaction components including hydrogen and isobutane to volatilize from the product to thereby provide the desired reaction product.

The specific correlation of conditions to be utilized with any specific catalyst of the present invention can be determined by one of ordinary skill in the art with comparative ease. Thus, for example, the tertiary butyl alcohol feedstock should be analyzed prior to catalytic treatment to determine the level of contamination by tertiary butyl hydroperoxide, ditertiary butyl peroxide, acetone, methanol and isobutylene. If there is an insufficient reduction of the hydroperoxides such that a significant amount (e.g., more than about 0.1 wt. %) of tertiary butyl hydroperoxide and/or ditertiary butyl peroxide is still present, the reaction conditions are not sufficiently severe, and should be increased such as, for example, by increasing reaction temperature or contact time in order to obtain the desired reduction of the tertiary butyl hydroperoxide.

If, on the other hand, there is a significant increase in the level of contamination of acetone, isobutylene and/or methanol, the reaction conditions are too severe for the particular catalyst and the reaction conditions should be ameliorated (e.g., by reducing contact time or temperature).

WORKING EXAMPLES Example A Catalyst Preparation

5676-72 Ni-Cu-Cr-Fe Catalyst Preparation

A solution composed of nickel (II) nitrate hexahydrate (9.32 kg, 32 mol), copper (II) nitrate hydrate (2.68 kg, 11.5 mol), chromium (III) nitrate nonahydrate (770 g, 1.92 mol) and iron (III) nitrate nonahydrate (1.81 kg, 4.49 mol) in 24 L of deionized (DI) water and a solution of the sodium carbonate (6.20 kg, 58.5 mol) in 32 L of DI water were added simultaneously to 19 L of rapidly stirred DI water at 60°-70° C. The additions took place over 3 hours. The rates of addition were adjusted so the pH of the solution remained between 7 and 8. Approximately 2 L (5%) of the carbonate solution was not added to the mixture. After stirring for one hour at 60°-70° C., the precipitated carbonates were removed by filtration. The solid was washed to remove sodium salts by slurrying with 45 L of fresh DI water and heating the resultant slurry to 70° C. with rapid stirring, followed by filtration. The washing and filtration steps were repeated five times. The metal carbonate mixture was dried in air at 110° C. and then calcined at 400° C. (5 hr. in several batches). A portion of the resultant metal oxide mixture was reduced in a hydrogen/nitrogen gas stream at 300° C., followed by partial oxidation at 25°-65° C. with a stream of air/nitrogen to stabilize the catalyst to atmospheric conditions. Graphite (1%) was added to a portion of the reduced and stabilized catalyst and this material was formed into 1/8 in. diameter×1/8 in. pellets. The catalyst was found to contain 51.2 wt. % Ni, 17.4 wt. % Cu, 2.9 wt. % Cr and 8.2 wt. % Fe.

5676-66 Ni-Cu-Cr-Fe Catalyst Preparation

Essentially the same amounts of materials and procedures were used as described in 5676-72 (above) in the preparation of this Ni-Cu-Cr-Fe catalyst, except that only 75% of the sodium carbonate solution was added and, consequently, not all of the nickel precipitated. The resultant catalyst contained 45.3 wt. % Ni, 26.7 wt. % Cu, 3.4 wt. % Cr and 9.9 wt. % Fe. A portion of the catalyst was formed into 1/8 in. diameter×1/8 in. pellets.

I. Equipment and Procedures

In all cases, these evaluations were performed in a 100 cc reactor constructed of 1/2 inch stainless steel tubing 17 inches long connected to a 1/8 inch feed and effluent lines with swagelok fittings. The reactor tube was situated inside of a 3×3 inch aluminum block which was heated electrically with four 1000 watt strip heaters. Temperature control was achieved with a Thermoelectric controller monitoring thermocouples attached to the skin of the reactor body. The feed was charged to the reactor system with a Beckman 110A L.C. pump. The reactor effluent was collected in a glass jug and sampled after the system and lined-out at the prescribed temperature for at least 2.5 hours.

The catalysts that were used in the working examples are listed in Table I together with a brief description of their composition.

                  TABLE I                                                          ______________________________________                                         Catalysts for Peroxide Decomposition                                           Code  Catalyst Description                                                     ______________________________________                                         AA    25% Cobalt on a proprietary silica-alumina                                     support, 1/8" extrusions                                                 BB    Unsupported manganese catalyst, 1/8" tablets                             CC    19% W, 6% Ni on silica support, 3/16" extrusions                         DD    10% V.sub.2 O.sub.5 on a silica-alumina support, 3/16"                         extrusions                                                               EE    Unsupported 55% Mo and 11% Fe, 1/8" tablets                                    (As moles of metals and metal oxides)                                    FF    Copper Chromite (79% CuO, 17% Cr.sub.2 O.sub.3), 1/8" tablets            GG    Ni 30.7%, Cu 12.6%, Fe 3.3%, Cr 0.64% (as moles of                             metals and metal oxides)                                                 HH    0.5% Rh on Alumina, 1/8" pellets                                         II    45% Ni, 5% Co, 4.5% Cu on 50% Silica, 1/8" tablets                       JJ    58% Fe.sub.2 O.sub.3, 23% K.sub.2 CO.sub.3, 5% Ce.sub.2 O.sub.3,               2.5% MoO.sub.3,                                                                1/8" extrusions                                                          KK    39% CuO, 8.5% Cr.sub.2 O.sub.3 on 50% SiO.sub.2, 1/8" tablets            LL    49.1% Ni, 13.9% Cu, 1.1% Cr, 17.4T Fe                                    MM    5676-72, See catalyst preparation                                        NN    5676-66, See catalyst preparation                                        OO    50.0% Ni, 15.0% Cu, 0.6% Cr                                              RR    58% Fe.sub.2 O.sub.3, 33% K.sub.2 CO.sub.3, 5% Ce.sub.2 O.sub.3,               2.5% MoO.sub.3,                                                                1/16" extrusions                                                         SS    89% Fe.sub.2 O.sub.3, 9% Cr.sub.2 O.sub.3, irregular                     TT    13 X Molecular sieves, 1/16" pellets                                     VV    0.44% Fe, 0.10% Cr, 0.21% Cu, 1% Ni on 97% SiO.sub.2,                          1/8" tablets                                                             XX    77% Ni, 12% Cu, 2% Cr, 1/8" extrusions                                   YY    56.5% Ni, 20.3% Cu, 3.2% Cr, 8.5% Mo                                     ______________________________________                                    

Example 1-A

In a first series of experiments a simulated tertiary butyl alcohol feedstock having the contamination levels listed for notebook No. 5787-76-1 in Table II was used as the feedstock.

In run 6064-60-1, the feedstock was heated in the reactor at a temperature of about 160° C. and a pressure of about 520 psig., being passed to the reactor at the rate of about 0.9 lbs/hr. As will be noted from Table II, there was a significant reduction in the level of tertiary butyl hydroperoxide contamination, but only a minor decrease in the level of contamination due to ditertiary butyl peroxide. Note also there was a significant increase in the level of contamination due to the formation of acetone.

The next series of fourteen sets of runs were made using the catalysts, as identified in Table I, under the reaction conditions noted in Table II with the results that are also there noted. This series of tests was, essentially, a screening test involving a wide variety of commercially available catalyst together with catalysts prepared in our laboratories. Thus, the catalysts included a supported cobalt catalyst (catalyst AA), a manganese catalyst (catalyst BB), a tungsten catalyst (catalyst CC), a vanadia catalyst (catalyst DD), a molybdena catalyst (catalyst EE), two copper chromite catalysts (catalysts FF and KK), a rhodium on alumina catalyst (catalyst HH), a catalyst containing three metallic oxides (catalyst II), a promoted iron oxide catalyst (catalyst JJ), a nickel, copper, chromia catalyst (catalyst OO), a promoted iron oxide catalyst (catalyst RR), a promoted chromia catalyst (catalyst SS) and a molecular sieve catalyst (catalyst TT). In addition, catalysts GG and LL of the present invention were also evaluated.

                                      TABLE II                                     __________________________________________________________________________     Catalytic Decomposition of Peroxides in tert-Butyl Alcohol                     N.B. Cat.                                                                              Temp.                                                                              Feed                                                                               Pressure                                                                            H.sub.2 O                                                                           TBHP Products by GC Analysis, Wt. %                  Number                                                                              Code                                                                              (°C.)                                                                       #/Hr                                                                               (psig)                                                                              (wt. %)                                                                             (ppm)                                                                               DTBP                                                                               Acetone                                                                             MeOH                                                                               IB=                                __________________________________________________________________________     5787-76-1                                                                           (Feed)          1.7  1555 0.117                                                                              0.002                                                                               0.003                                                                              ˜0                           6064-60-1                                                                           None                                                                              160 0.90                                                                               520  1.8  227  0.095                                                                              0.033                                                                               0.002                                                                              ˜0                           6064-77-1                                                                           AA  80 1.04                                                                               500  1.7  113  0.118                                                                              0.010                                                                               ˜0                                                                           ˜0                           2       120 0.99                                                                               500  1.7  6.13 0.118                                                                              0.016                                                                               0.001                                                                               0.00077                           3       160 1.00                                                                               500  1.7  4.76 0.100                                                                              0.033                                                                               0.002                                                                              0.010                              6064-82-1                                                                           BB  80 1.02                                                                               500  1.77 113  0.116                                                                              0.010                                                                               ˜0                                                                           ˜0                           2       120 1.00                                                                               500  1.74 10.99                                                                               0.116                                                                              0.017                                                                               ˜0                                                                           ˜0                           3       160 1.00                                                                               500  1.72 3.71 0.102                                                                              0.036                                                                               0.001                                                                               0.00097                           6064-84-1                                                                           CC 120 0.99                                                                               500  1.74 238  0.107                                                                              0.002                                                                               ˜0                                                                           0.003                              2        80 1.02                                                                               500  1.72 162  0.116                                                                                0.00097                                                                           ˜0                                                                           ˜0                           3       160 1.00                                                                               500  1.90 201  0.101                                                                              0.020                                                                               0.001                                                                              0.331                              6064-87-1                                                                           DD  80 0.99                                                                               500  2.7  692  0.117                                                                              0.004                                                                               0.002                                                                              0.284                              2       120 0.96                                                                               500  3.9  178  0.121                                                                              0.019                                                                               0.003                                                                              2.330                              3       160 0.95                                                                               500  8.8  12.73                                                                               0.111                                                                              0.044                                                                               0.002                                                                              3.853                              6064-90-1                                                                           EE  80 0.91                                                                               500  1.7  563  0.119                                                                              0.003                                                                               0.002                                                                              0.029                              2       120 1.00                                                                               500  2.2  488  0.119                                                                              0.003                                                                               0.002                                                                              1.021                              3       160 1.02                                                                               500  6.6  136  0.116                                                                              0.026                                                                               0.001                                                                              4.588                              6064-92-1                                                                           FF  80 1.02                                                                               500  1.7  282  0.116                                                                              0.004                                                                               0.002                                                                              0.003                              2       120 0.99                                                                               500  1.7  184  0.115                                                                              0.012                                                                               0.004                                                                              0.001                              3       160 1.00                                                                               500  1.8  15.8 0.102                                                                              0.051                                                                               0.006                                                                              0.011                              6064-93-1                                                                           GG  80 1.02                                                                               500  1.7  195  0.102                                                                              0.007                                                                               0.004                                                                              0.005                              2       120 1.00                                                                               500  1.7  12.5 0.089                                                                              0.009                                                                               0.004                                                                              0.002                              3       160 1.00                                                                               500  1.7  8.48 0.032                                                                              0.051                                                                               0.004                                                                              0.038                              6064-96-1                                                                           HH  80 0.95                                                                               500  1.73 57.7 0.107                                                                              0.011                                                                               0.003                                                                              ˜0                           2       120 1.00                                                                               500  1.71 21.6 0.105                                                                              0.015                                                                               0.003                                                                              ˜0                           3       160 1.00                                                                               500  1.71 11.7 0.092                                                                              0.028                                                                               0.003                                                                              0.001                              6064-98-1                                                                           II  80 1.04                                                                               500  1.70 103.6                                                                               0.119                                                                              0.014                                                                               0.003                                                                              ˜ 0                          2       120 1.01                                                                               500  1.70 23.9 0.107                                                                              0.018                                                                               0.003                                                                              0.014                              3       160 1.00                                                                               500  1.90 12.4 0.087                                                                              0.028                                                                               0.004                                                                              0.368                              6064-99-1                                                                           JJ  80 1.05                                                                               500  1.63 219  0.105                                                                              0.003                                                                               0.003                                                                              0.002                              2       120 1.00                                                                               500  1.69 203  0.106                                                                              0.005                                                                               0.003                                                                              ˜0                           3       160 0.92                                                                               500  1.71 223  0.094                                                                              0.024                                                                               0.003                                                                              0.001                              6064-100-1                                                                          KK  80 1.01                                                                               500  1.74 203  0.105                                                                              0.003                                                                               0.003                                                                              ˜0                           2       120 1.00                                                                               500  1.72 212  0.106                                                                              0.009                                                                               0.004                                                                              0.003                              3       160 1.03                                                                               500  1.73 14.9 0.082                                                                              0.061                                                                               0.008                                                                              0.033                              6089-6-1                                                                            GG 160 1.04                                                                               500  1.71 22.1 0.026                                                                              0.044                                                                               0.004                                                                              0.045                              2       200 1.02                                                                               500  2.03 21.6 0.008                                                                              0.266                                                                               ˜0                                                                           0.575                              3       240 1.02                                                                               500  4.68 10.6 0.004                                                                              0.302                                                                               0.001                                                                              3.366                              6089-7-1                                                                            GG 160 0.21                                                                               500  1.97 25.5 0.012                                                                              0.165                                                                               0.002                                                                              0.159                              2       200 0.25                                                                               500  2.23 22.1 0.003                                                                              0.246                                                                               ˜0                                                                           1.909                              3       240 0.28                                                                               500  --   14.0 0.003                                                                              0.511                                                                               ˜0                                                                           1.934                              6089-12-1                                                                           GG 140 0.23                                                                               500  2.15 20.7 0.014                                                                              0.097                                                                               0.003                                                                              0.321                              2       180 0.22                                                                               500  4.08 22.5 0.006                                                                              0.240                                                                               ˜0                                                                           3.319                              __________________________________________________________________________

Turning now to Table II, it will be noted that in all instances there was a reduction in the level of contamination of tertiary butyl hydroperoxide. However, in certain runs (e.g., 6064-84-1, 6064-87-1, 6064-90-1 and 6064-90-2) the contamination level was greater than the level accomplished by straight thermal decomposition at 160° C. in run 6064-60-1.

However, insofar as the reduction of the level of ditertiary butyl peroxide is concerned, the only catalysts that reduce the level of ditertiary butyl peroxide below that obtainable by straight thermal decomposition (run 6064-60-1) were catalysts GG, HH, II, JJ and KK. Of this group of catalysts, however, only the use of catalyst GG of the present invention result in a reduction of ditertiary butyl peroxide contamination to less than 0.05 wt. %, and this was accomplished only in run 6089-19-3.

In view of the favorable results obtained at the higher temperature with catalyst GG, three additional runs were made scanning a higher bracket of temperatures ranging from 140°-240° C. Note from run 6089-6, triplicate runs 6089-7 and duplicate runs 6089-12 that in all instances a very low level of contamination of ditertiary butyl peroxide was achieved. However, when the temperature was more than about 160° C. an unacceptable level of isobutylene contamination was obtained. This is shown by run 6089-6-1, 6089-6-2 and 6089-6-3. Longer contact times still further reduced the level of contamination of ditertiary butyl peroxide but resulted in unacceptably high levels of isobutylene contamination as shown by triplicate runs 6089-7 and duplicate runs 6089-12.

Example 1-B

A further series of tests were conducted using a variety of catalyst compositions of the present invention together with reference catalysts of closely related composition. For this series of tests, however, tertiary butyl hydroperoxide was eliminated from the simulated feedstock because it had already been demonstrated that a catalyst which is effective for reducing the level of contamination of ditertiary butyl peroxide will also be effective for reducing the level of contamination of tertiary butyl hydroperoxide. The catalysts tested and the results obtained are summarized in Table III.

                                      TABLE III                                    __________________________________________________________________________     Catalytic Decomposition of Peroxides in tert-Butyl Alcohol                     N.B.  Cat.                                                                              Temp.                                                                              Feed                                                                              Press.                                                                             H.sub.2 O                                                                          Products by GC Analysis, Wt. %                         Number                                                                               Code                                                                              (°C.)                                                                       #/Hr                                                                              (psig)                                                                             wt. %                                                                              DTBP                                                                               Acetone                                                                             MeOH                                                                               IB═                                   __________________________________________________________________________     5787-80-1                                                                            (Feed)        0.11                                                                               0.839                                                                              0.002                                                                               0.003                                                                              ˜0                                  6089-19-1                                                                            GG 140 0.94                                                                              500 0.22                                                                               0.409                                                                              0.111                                                                               0.001                                                                              0.185                                     2        160 0.98                                                                              500 0.38                                                                               0.196                                                                              0.176                                                                               0.003                                                                              0.643                                     3        180 1.00                                                                              500 0.89                                                                               0.045                                                                              0.265                                                                               0.002                                                                              1.498                                     6089-20-1                                                                            GG 140 0.19                                                                              500 0.47                                                                               0.010                                                                              0.345                                                                               0.002                                                                              0.713                                     2        160 0.20                                                                              500 1.02                                                                               0.006                                                                              0.345                                                                               0.002                                                                              2.313                                     3        180 0.21                                                                              500 2.51                                                                               0.008                                                                              0.357                                                                               0.004                                                                              5.100                                     6089-35-1                                                                            LL 140 0.21                                                                              500 0.08                                                                               0.118                                                                              0.076                                                                               0.006                                                                              0.009                                     2        150 0.22                                                                              500 0.08                                                                               0.022                                                                              0.122                                                                               0.005                                                                              0.013                                     3        160 0.21                                                                              500 0.13                                                                               0.017                                                                              0.211                                                                               0.006                                                                              0.014                                     6089-36-1                                                                            LL 140 0.95                                                                              500 0.09                                                                               0.406                                                                              0.022                                                                               0.003                                                                              0.004                                     2        150 0.99                                                                              500 0.06                                                                               0.316                                                                              0.035                                                                               0.003                                                                              0.004                                     3        160 1.00                                                                              500 0.15                                                                               0.190                                                                              0.067                                                                               0.003                                                                              0.006                                     6089-42-1                                                                            LL 170 1.03                                                                              500 0.10                                                                               0.195                                                                              0.165                                                                               0.005                                                                              0.005                                     2        180 1.04                                                                              500 0.10                                                                               0.075                                                                              0.241                                                                               0.005                                                                              0.012                                     3        190 1.02                                                                              500 0.13                                                                               0.017                                                                              0.321                                                                               0.004                                                                              0.042                                     4        200 0.98                                                                              500 0.21                                                                               0.018                                                                              0.399                                                                               0.002                                                                              0.077                                     6089-39-1                                                                            MM 140 0.26                                                                              500 0.27                                                                               0.333                                                                              0.074                                                                               0.003                                                                              0.003                                     2        150 0.20                                                                              500 0.47                                                                               0.093                                                                              0.259                                                                               0.004                                                                              0.005                                     3        160 0.20                                                                              500 0.35                                                                               0.019                                                                              0.408                                                                               0.003                                                                              0.009                                     6089-40-1                                                                            MM 140 1.02                                                                              500 0.11                                                                               0.680                                                                              0.027                                                                               ˜0                                                                           0.001                                     2        150 0.98                                                                              500 0.13                                                                               0.618                                                                              0.050                                                                               ˜0                                                                           0.002                                     3        160 1.00                                                                              500 0.10                                                                               0.522                                                                              0.090                                                                               ˜0                                                                           0.003                                     6787-80-2                                                                            (Feed)        0.12                                                                               0.835                                                                              0.002                                                                               0.002                                                                              0.001                                     6089-49-1                                                                            MM 170 0.96                                                                              500 --  0.362                                                                              0.154                                                                               0.001                                                                              0.004                                     2        180 0.97                                                                              500 0.12                                                                               0.221                                                                              0.235                                                                               ˜0                                                                           0.005                                     3        190 0.96                                                                              500 0.14                                                                               0.094                                                                              0.322                                                                               0.001                                                                              0.004                                     4        200 0.97                                                                              500 0.18                                                                               0.027                                                                              0.448                                                                               ˜0                                                                           0.014                                     6089-51-1                                                                            NN 130 0.20                                                                              500 0.29                                                                               0.356                                                                              0.064                                                                               ˜0                                                                           0.002                                     2        140 0.21                                                                              500 0.07                                                                               0.062                                                                              0.059                                                                               ˜0                                                                           0.002                                     3        150 0.19                                                                              500 0.04                                                                               0.053                                                                              0.094                                                                               ˜0                                                                           0.005                                     4        160 0.23                                                                              500 0.07                                                                               0.003                                                                              0.100                                                                               0.001                                                                              0.006                                     6089-52-1                                                                               130 0.98                                                                              500 0.06                                                                               0.613                                                                              0.017                                                                               ˜0                                                                           0.001                                     2        140 0.97                                                                              500 0.09                                                                               0.532                                                                              0.029                                                                               ˜0                                                                           0.001                                     3        150 1.04                                                                              500 0.06                                                                               0.433                                                                              0.045                                                                               ˜0                                                                           0.001                                     4        160 0.99                                                                              500 0.04                                                                               0.304                                                                              0.075                                                                               0.001                                                                              0.002                                     6089-53-1                                                                               170 1.07                                                                              500 0.06                                                                               0.218                                                                              0.124                                                                               0.001                                                                              0.004                                     2        180 1.04                                                                              500 0.12                                                                               0.102                                                                              0.210                                                                               ˜0                                                                           0.007                                     3        190 1.03                                                                              500 0.04                                                                               0.030                                                                              0.273                                                                               0.002                                                                              0.011                                     4        200 1.00                                                                              500 0.06                                                                               0.011                                                                              0.293                                                                               0.001                                                                              0.017                                     6089-59-1                                                                            OO 130 0.20                                                                              500 0.07                                                                               0.596                                                                              0.051                                                                               0.002                                                                              0.045                                     2        140 0.21                                                                              500 0.12                                                                               0.507                                                                              0.088                                                                               0.004                                                                              0.070                                     3        150 0.23                                                                              500 0.14                                                                               0.359                                                                              0.168                                                                               0.006                                                                              0.115                                     4        160 0.22                                                                              500 0.18                                                                               0.101                                                                              0.202                                                                               0.006                                                                              0.162                                     6089-60-1                                                                               130 1.08                                                                              500 0.01                                                                               0.783                                                                              0.011                                                                               ˜0                                                                           0.012                                     2        140 1.10                                                                              500 0.01                                                                               0.727                                                                              0.023                                                                               0.001                                                                              0.027                                     3        150 1.08                                                                              500 0.17                                                                               0.599                                                                              0.074                                                                               0.002                                                                              0.072                                     4        160 1.08                                                                              500 0.16                                                                               0.564                                                                              0.096                                                                               0.003                                                                              0.078                                     6089-61-1                                                                               170 1.02                                                                              500 0.03                                                                               0.457                                                                              0.162                                                                               0.004                                                                              0.089                                     2        180 0.98                                                                              500 0.17                                                                               0.292                                                                              0.269                                                                               0.005                                                                              0.156                                     3        190 1.06                                                                              500 0.18                                                                               0.164                                                                              0.351                                                                               0.006                                                                              0.167                                     4        200 1.03                                                                              500 0.24                                                                               0.025                                                                              0.450                                                                               0.006                                                                              0.319                                     5787-100-2                                                                           (Feed)        0.05                                                                               0.812                                                                              0.002                                                                               ˜0                                                                           0.002                                     6089-73-1                                                                            RR 130 0.22                                                                              500 0.14                                                                               0.803                                                                              0.035                                                                               ˜0                                                                            0.0008                                   2        140 0.19                                                                              500 0.10                                                                               0.716                                                                              0.121                                                                                0.0006                                                                            0.001                                     3        150 0.18                                                                              500 0.21                                                                               0.570                                                                              0.241                                                                               ˜0                                                                           0.001                                     4        160 0.20                                                                              500 0.11                                                                               0.326                                                                              0.450                                                                                0.0004                                                                             0.0008                                   6089-74-1                                                                               130 1.00                                                                              500 0.08                                                                               0.858                                                                              0.009                                                                                0.0008                                                                             0.0008                                   2        140 1.00                                                                              500 0.11                                                                               0.843                                                                              0.020                                                                               0.001                                                                               0.0009                                   3        150 0.97                                                                              500 0.11                                                                               0.813                                                                              0.045                                                                                0.0009                                                                            0.001                                     4        160 0.98                                                                              500 0.10                                                                               0.731                                                                              0.116                                                                                0.0008                                                                            0.002                                     5787-100-4                                                                           (Feed)        0.07                                                                               0.896                                                                              0.002                                                                               ˜0                                                                           0.002                                     6089-75-1                                                                               170 0.98                                                                              500 0.09                                                                               0.591                                                                              0.233                                                                                0.0007                                                                            0.002                                     2        180 1.02                                                                              500 0.06                                                                               0.404                                                                              0.454                                                                               0.001                                                                              0.002                                     3        190 0.96                                                                              500 0.16                                                                               0.148                                                                              0.681                                                                                0.0008                                                                            0.002                                     4        200 0.96                                                                              500 0.06                                                                               0.021                                                                              0.658                                                                                0.0006                                                                             0.0008                                   6089-76-1                                                                            SS 130 0.25                                                                              500 0.14                                                                               1.313                                                                              0.052                                                                               0.001                                                                              0.007                                     2        140 0.23                                                                              500 0.11                                                                               0.627                                                                              0.068                                                                                0.0005                                                                            0.013                                     3        150 0.19                                                                              500 0.09                                                                               0.622                                                                              0.184                                                                                0.0009                                                                            0.017                                     4        160 0.22                                                                              500 0.10                                                                               0.305                                                                              0.326                                                                               0.001                                                                              0.022                                     6089-77-1                                                                               130 0.95                                                                              500 0.12                                                                               0.995                                                                              0.022                                                                                0.0005                                                                            0.002                                     2        140 0.99                                                                              500 0.09                                                                               0.980                                                                              0.028                                                                                0.0006                                                                            0.003                                     3        150 0.98                                                                              500 0.08                                                                               0.929                                                                              0.052                                                                               0.001                                                                              0.005                                     4        160 0.97                                                                              500 0.08                                                                               0.841                                                                              0.121                                                                                0.0007                                                                            0.010                                     6089-78-1                                                                               170 1.00                                                                              500 0.07                                                                               0.675                                                                              0.231                                                                                0.0008                                                                            0.015                                     2        180 1.02                                                                              500 0.11                                                                               0.443                                                                              0.384                                                                               0.001                                                                              0.024                                     3        190 0.99                                                                              500 0.11                                                                               0.158                                                                              0.559                                                                               ˜0                                                                           0.041                                     4        200 1.00                                                                              500 0.17                                                                               0.018                                                                              0.643                                                                               0.002                                                                              0.111                                     6123-1-1                                                                             (Feed)        0.06                                                                               0.843                                                                              0.002                                                                               ˜0                                                                           0.001                                     6129-39-1                                                                            XX 130 0.22                                                                              500 0.17                                                                               0.416                                                                              0.072                                                                               0.003                                                                              0.011                                     2        140 0.18                                                                              500 0.14                                                                               0.189                                                                              0.196                                                                               0.002                                                                              0.014                                     3        150 0.22                                                                              500 0.19                                                                               0.137                                                                              0.277                                                                               0.003                                                                              0.066                                     4        160 0.17                                                                              500 0.32                                                                               0.015                                                                              0.346                                                                               0.002                                                                              0.214                                     6129-40-1                                                                               130 0.97                                                                              500 0.09                                                                               0.729                                                                              0.058                                                                               ˜0                                                                           0.007                                     2        140 1.00                                                                              500 0.09                                                                               0.731                                                                              0.071                                                                               ˜0                                                                           0.017                                     3        150 0.98                                                                              500 0.11                                                                               0.692                                                                              0.089                                                                               ˜0                                                                           0.033                                     4        160 1.00                                                                              500 0.15                                                                               0.587                                                                              0.152                                                                               ˜0                                                                           0.071                                     6129-41-1                                                                               170 0.98                                                                              500 0.28                                                                               0.732                                                                              0.382                                                                               ˜0                                                                           0.104                                     2        180 0.96                                                                              500 0.31                                                                               0.250                                                                              0.358                                                                               0.004                                                                              0.178                                     3        190 1.02                                                                              500 0.32                                                                               0.046                                                                              0.332                                                                               ˜0                                                                           0.266                                     4        200 1.03                                                                              500 0.39                                                                               0.004                                                                              0.262                                                                               ˜0                                                                           0.234                                     6129-74-1                                                                            YY 130 0.20                                                                              500 0.12                                                                               0.003                                                                              0.064                                                                               0.006                                                                              0.111                                     2        140 0.19                                                                              500 0.19                                                                               0.002                                                                              0.072                                                                               0.005                                                                              0.289                                     3        150 0.19                                                                              500 0.35                                                                               ˜0                                                                           0.072                                                                               0.007                                                                              0.290                                     4        160 0.20                                                                              500 0.47                                                                               ˜0                                                                           0.093                                                                               0.007                                                                              0.865                                     6129-75-1                                                                               130 1.00                                                                              500 0.15                                                                               0.564                                                                              0.022                                                                               0.002                                                                              0.032                                     2        140 1.00                                                                              500 0.12                                                                               0.313                                                                              0.051                                                                               0.005                                                                              0.069                                     3        150 0.93                                                                              500 0.30                                                                               0.015                                                                              0.219                                                                               ˜0                                                                           0.184                                     4        160 0.95                                                                              500 0.06                                                                               0.053                                                                              0.094                                                                               0.009                                                                              0.194                                     6129-76-1                                                                               170 1.16                                                                              500 0.32                                                                               0.033                                                                              0.155                                                                               ˜0                                                                           0.432                                     2        180 1.05                                                                              500 0.20                                                                               0.125                                                                              0.119                                                                               0.010                                                                              0.185                                     3        190 1.05                                                                              500 0.45                                                                               0.009                                                                              0.182                                                                               0.001                                                                              0.729                                     4        200 1.01                                                                              500 0.73                                                                               0.003                                                                              0.226                                                                               0.011                                                                              1.239                                     6123-2-2                                                                             (Feed)        0.05                                                                               0.841                                                                              ˜0                                                                            ˜0                                                                           0.003                                     6129-7-1                                                                             TT 130 0.2                                                                               500 0.71                                                                               0.756                                                                              0.022                                                                               ˜0                                                                           0.251                                     2        140 0.2                                                                               500 0.39                                                                               0.710                                                                              0.050                                                                               ˜0                                                                           0.677                                     3        150 0.2                                                                               500 0.66                                                                               0.586                                                                              0.116                                                                               ˜0                                                                           1.234                                     4        160 0.2                                                                               500 1.30                                                                               0.335                                                                              0.258                                                                               ˜0                                                                           2.154                                     6129-8-1 130 1.0                                                                               500 0.10                                                                               0.784                                                                              ˜0                                                                            ˜0                                                                           0.167                                     2        140 1.0                                                                               500 0.20                                                                               0.776                                                                              0.013                                                                               ˜0                                                                           0.368                                     3        150 1.0                                                                               500 0.30                                                                               0.754                                                                              0.028                                                                               ˜0                                                                           0.699                                     4        160 1.0                                                                               500 0.60                                                                               0.687                                                                              0.064                                                                               ˜0                                                                           1.359                                     6129-9-1 170 1.0                                                                               500 1.00                                                                               0.570                                                                              0.135                                                                               ˜0                                                                           1.501                                     2        180 1.0                                                                               500 1.40                                                                               0.386                                                                              0.241                                                                               ˜0                                                                           2.017                                     3        190 1.0                                                                               500 2.00                                                                               0.150                                                                              0.375                                                                               ˜0                                                                           2.615                                     4        200 1.0                                                                               500 2.60                                                                               0.035                                                                              0.469                                                                               ˜0                                                                           4.144                                     6129-35-1                                                                            VV 130 0.2                                                                               500 0.07                                                                               0.667                                                                              0.053                                                                               0.002                                                                              0.002                                     2        140 0.2                                                                               500 0.07                                                                               0.516                                                                              0.124                                                                               0.004                                                                              0.004                                     3        150 0.2                                                                               500 0.08                                                                               0.367                                                                              0.224                                                                               ˜0                                                                           0.007                                     4        160 0.2                                                                               500 0.07                                                                               0.144                                                                              0.371                                                                               ˜0                                                                           0.009                                     6129-36-1                                                                               130 1.0                                                                               500 0.06                                                                               0.771                                                                              0.011                                                                               ˜0                                                                           0.001                                     2        140 1.0                                                                               500 0.05                                                                               0.742                                                                              0.025                                                                                0.0004                                                                            0.002                                     3        150 1.0                                                                               500 0.05                                                                               0.688                                                                              0.058                                                                               0.001                                                                              0.003                                     4        160 1.0                                                                               500 0.06                                                                               0.590                                                                              0.124                                                                               0.002                                                                              0.006                                     6129-37-1                                                                               170 1.0                                                                               500 0.04                                                                               0.436                                                                              0.226                                                                               0.004                                                                              0.008                                     2        180 1.0                                                                               500 0.06                                                                               0.218                                                                              0.385                                                                               0.005                                                                              0.009                                     3        190 1.0                                                                               500 0.07                                                                               0.055                                                                              0.497                                                                               0.005                                                                              0.009                                     4        200 1.0                                                                               500 0.07                                                                               0.011                                                                              0.540                                                                               0.005                                                                              0.011                                     6123-1-2                                                                             (Feed)        0.03                                                                               0.843                                                                              0.002                                                                               ˜0                                                                           0.001                                     6129-44-1                                                                            LL 140 0.5                                                                               500 0.03                                                                               0.377                                                                              0.047                                                                               ˜0                                                                           0.005                                     2        160 0.5                                                                               500 0.17                                                                               0.115                                                                              0.119                                                                               ˜0                                                                           0.008                                     3        200 0.5                                                                               500 0.09                                                                               0.005                                                                              0.247                                                                               ˜0                                                                           0.092                                     6123-4-1                                                                             (Feed)        0.04                                                                               0.434                                                                              0.011                                                                               ˜0                                                                           0.009                                     6129-45-1                                                                               140 0.2                                                                               500 0.10                                                                               0.012                                                                              0.104                                                                               ˜0                                                                           0.002                                     2        160 0.2                                                                               500 0.09                                                                               0.008                                                                              0.041                                                                               ˜0                                                                           ˜0                                  3        180 0.2                                                                               500 0.19                                                                               0.006                                                                              0.251                                                                               ˜0                                                                           0.084                                     4        200 0.2                                                                               500 0.50                                                                               0.007                                                                              0.268                                                                               ˜0                                                                           0.417                                     6129-46-1                                                                               140 0.5                                                                               500 0.05                                                                               0.170                                                                              0.065                                                                               ˜0                                                                           0.007                                     2        160 0.5                                                                               500 0.09                                                                               0.015                                                                              0.161                                                                               ˜0                                                                           0.012                                     3        180 0.5                                                                               500 0.16                                                                               0.011                                                                              0.248                                                                               ˜0                                                                           0.026                                     4        200 0.5                                                                               500 0.25                                                                               0.006                                                                              0.256                                                                               ˜0                                                                           0.159                                     6129-47-1                                                                               140 1.0                                                                               500 0.07                                                                               0.218                                                                              0.066                                                                               ˜0                                                                           0.004                                     2        160 1.0                                                                               500 0.06                                                                               0.125                                                                              0.108                                                                               ˜0                                                                           0.005                                     3        180 1.0                                                                               500 0.07                                                                               0.035                                                                              0.172                                                                               ˜0                                                                           0.007                                     4        200 1.0                                                                               500 0.10                                                                               0.008                                                                              0.217                                                                               ˜0                                                                           0.047                                     __________________________________________________________________________

As shown in Table III, when catalyst GG was again evaluated, good results were obtained in runs 6089-19-1 and 6089-19-2 insofar as the reduction in the level of contamination of ditertiary butyl peroxide was concerned, with only minor increases in the level of contamination of acetone, methanol and isobutylene. In run 6089-3, conducted at 180° C., an unacceptably high level of contamination of isobutylene was noted.

In triplicate run 6089-20, the feed rate was decreased from about 1 lb/hr to about 0.2 lbs/hr. There was a further reduction in the level of contamination by ditertiary butyl peroxide, but they were unsatisfactory results insofar as contamination by acetone and isobutylene are concerned.

Triplicate run 6089-36 and triplicate run 6089-42 are directed to the evaluation of a nickel, copper, chromia catalyst supported on iron (catalyst LL). With this catalyst, good reductions in the level of contamination by ditertiary butyl peroxide were obtained at temperatures of 140°-160° and feed rates of about 0.2 lbs/hr (runs 6089-35-1, 6089-35-2 and 6089-35-3). Runs 6089-36-1, 6089-36-2 and 6089-36-3 were conducted at feed rates of about 1 lb/hr and again, an acceptable level of reduction of contamination by ditertiary butyl peroxide was obtained, although not so good as the previous run, but much better results insofar as contamination by acetone, methanol and isobutylene are concerned. Good results were also obtained in quadruplicate runs 6089-42 using higher temperatures ranging from 170° to 200° C.

The use of a coprecipitated nickel, copper, chromia, iron catalyst prepared in our laboratories (catalyst MM) resulted in good reductions in the contamination level of ditertiary butyl peroxide without a significant increase in the level of contamination by acetone, methanol and isobutylene. This was true for a temperature range of from 140° through 200° C. (see run 6089-49).

A similar laboratory preparation of a nickel, copper, chromia, iron oxide catalyst but with different proportions of the metals (catalyst NN) also gave favorable results as reported in runs 6089-51, 6089-52 and 6089-53 wherein the temperature ranged from 130° to 200° and feed rates of both 0.2 lbs/hr and 1 lb/hr were used. In contrast, a nickel, copper, chromia catalyst (catalyst OO) resulted in a product containing a higher level of impurities attributable to ditertiary butyl peroxide and isobutylene (runs 6089-59, 6089-60 and 6089-61).

By way of comparison, in runs RR, a proprietary promoted iron oxide catalyst of United was evaluated. Good results were not obtained. Even at 160° C. and 0.2 #/hr liquid flow rate, 0.3% DTBP still remained. This is an unsatisfactory result. A chromia promoted iron oxide catalyst (catalyst SS) did not result in the favorable reduction of ditertiary butyl peroxide contamination level and, moreover, provided higher levels of contamination insofar as acetone and isobutylene are concerned.

A reference catalyst, nickel, copper, chromia (catalyst XX) was evaluated in runs 6129-39, 6129-40 and 6129-41. Higher levels of ditertiary butyl peroxide contamination in the product, as well as higher levels of isobutylene contamination were noted, as compared with the other catalyst. A molybdenum promoted nickel, copper, chromia catalyst was also evaluated (catalyst YY) in runs 6129-74, 6129-75 and 6129-76. Although very low levels of ditertiary butyl peroxide contamination were obtained, the levels of isobutylene contamination were excessive. When a molecular sieve was evaluated as a catalyst (catalyst TT) in runs 6129-7, 6129-8 and 6129-9, unacceptably high level of isobutylene contamination were noted. In contrast, with catalyst VV an iron, chromia, copper, nickel catalyst supported on silica (catalyst VV) good results were obtained insofar as isobutylene contamination is concerned. There was also moderate to low level of reduction of the contamination by ditertiary butyl peroxide.

Catalyst VV contained very low levels of Ni, Cu, Cr, Fe and was therefore not as active. The low levels of metals in this catalyst are outside our preferred catalyst composition ranges.

The foregoing examples are given by way of illustration only, and are not intended as limitations on the scope of this invention, as defined by the appended claims. 

Having thus described our invention, what is claimed is:
 1. A method for enhancing the motor fuel quality of a tertiary butyl alcohol feedstock contaminated with residual quantities of tertiary butyl hydroperoxide and ditertiary butyl peroxide, which comprises the steps of:a. contacting said feedstock in a reaction zone with a catalyst at a temperature of about 80° to about 220° C. for a period of time sufficient to substantially selectively reduce said tertiary butyl hydroperoxide and said ditertiary butyl peroxide to tertiary butyl alcohol, and b. recovering substantially hydroperoxide-free tertiary butyl alcohol from the products of said reaction, c. said catalyst being composed of a metals component consisting essentially of metallic nickel, copper, chromium and iron or the oxides of one or more of said metals in the proportions, on an oxygen-free basis, of about 30 to about 60 wt. % of nickel and about 5 to about 40 wt. % of copper in the weight ratio of about 2 to 3 parts of nickel per part of copper and also containing, based on the total weight of said metals of from about 1 to about 30 wt. % of iron and from about 0.5 to about 10 wt. % of chromium or a catalyst consisting essentially of from about 5 to about 50 wt. % of said metals component supported on, correspondingly, from about 50 to about 95 wt. % of a silica support.
 2. A method as in claim 1 wherein reaction is conducted at a temperature of about 110° to about 180° C.
 3. A method for enhancing the motor fuel quality of a tertiary butyl alcohol feedstock contaminated with from about 0.1 to about 5 wt. % of tertiary butyl hydroperoxide and from about 0.1 to about 5 wt. % of ditertiary butyl peroxide, and contaminating quantities of acetone, methanol and isobutylene which comprises the steps of:a. contacting said feedstock in a reaction zone with a catalyst at a temperature of about 110° to about 180° C. for a period of time sufficient to substantially selectively reduce said tertiary butyl hydroperoxide and said ditertiary butyl peroxide to tertiary butyl alcohol without significantly increasing the level of contamination of acetone, methanol and isobutylene, and b. recovering from the products of said reaction, tertiary butyl alcohol containing not more than about 100 ppm of tertiary butyl hydroperoxide, not more than about 100 ppm of ditertiary butyl peroxide, not more than about 3 wt. % of acetone and not more than about 0.5 wt. % of isobutylene, c. said catalyst being composed of a metals component consisting essentially of metallic nickel, copper, chromium and iron or the oxides of one or more of said metals in the proportions, on an oxygen-free basis, of about 30 to about 60 wt. % of nickel and about 5 to about 40 wt. % of copper in the weight ratio of about 2 to 3 parts of nickel per part of copper and also containing, based on the total weight of said metals of from about 1 to about 30 wt. % of iron and from about 0.5 to about 10 wt. % of chromium or a catalyst consisting essentially of from about 5 to about 50 wt. % of said metals component supported on, correspondingly, from about 50 to about 95 wt. % of a silica support.
 4. A method as in claim 3 wherein the catalyst is an unsupported catalyst.
 5. A method as in claim 3 wherein the catalyst is a silica-supported catalyst.
 6. A method for enhancing the motor fuel quality of a tertiary butyl alcohol feedstock obtained by the reaction of propylene with tertiary butyl hydroperoxide to form propylene oxide and said tertiary butyl alcohol feedstock, said tertiary butyl alcohol feedstock being contaminated with residual quantities of tertiary butyl hydroperoxide, ditertiary butyl peroxide, acetone, methanol and isobutylene said method comprising the steps of:a. contacting said feedstock in a reaction zone with a catalyst at a temperature of about 80° to about 160° C. for a period of time sufficient to substantially selectively reduce said tertiary butyl hydroperoxide and said ditertiary butyl peroxide to tertiary butyl alcohol, and b. recovering from the products of said reaction, product tertiary butyl alcohol containing not more than about 100 ppm of tertiary butyl hydroperoxide, not more than about 100 ppm of ditertiary butyl peroxide, not more than about 3 wt. % of acetone and not more than about 0.5 wt. % of isobutylene. c. said catalyst being composed of a metals component consisting essentially of metallic nickel, copper, chromium and iron or the oxides of one or more of said metals in the proportions, on an oxygen-free basis, of about 30 to about 60 wt. % of nickel and about 5 to about 40 wt. % of copper in the weight ratio of about 2 to 3 parts of nickel per part of copper and also containing, based on the total weight of said metals of from about 1 to about 30 wt. % of iron and from about 0.5 to about 10 wt. % of chromium or a catalyst consisting essentially of from about 5 to about 50 wt. % of said metals component supported on, correspondingly, from about 50 to about 95 wt. % of a silica support.
 7. A method as in claim 6 wherein the catalyst is a silica-supported catalyst.
 8. A method as in claim 6 wherein the catalyst is an unsupported catalyst.
 9. A method as in claim 8 wherein the catalyst contains about 30 to about 60 wt. % of nickel and about 5 to about 40 wt. % of copper in the weight ratio of about 2 to 3 parts of nickel per part of copper and also contains, based on the total weight of said metals of from about 1 to about 20 wt. % of iron and from about 1 to about 5 wt. % of chromium.
 10. A method as in claim 9 wherein the catalyst contains about 51.2 wt. % of nickel, about 17.4 wt. % of copper, about 8.2 wt. % of iron and about 2.9 wt. % of chromium.
 11. A method as in claim 9 wherein the catalyst contains about 45.3 wt. % of nickel, about 26.7 wt. % of copper, about 9.9 wt. % of iron and about 3.4 wt. % of chromium.
 12. A method as in claim 9 wherein the catalyst contains about 30.7 wt. % of nickel, about 12.6 wt. % of copper, about 3.3 wt. % of iron and about 0.64 wt. % of chromium.
 13. A method as in claim 9 wherein the catalyst contains about 49.1 wt. % of nickel, about 13.9 wt. % of copper, about 17.4 wt. % of iron and about 1.1 wt. % of chromium.
 14. A method as in claim 6 wherein the product tertiary butyl alcohol contains not more than about 10 ppm of tertiary butyl hydroperoxide, not more than about 100 ppm of ditertiary butyl peroxide, not more than about 1 wt. % of acetone and not more than about 0.5 wt. % of isobutylene,
 15. A method as in claim 14 wherein the catalyst is an unsupported catalyst containing about 51.2 wt. % of nickel, about 17.4 wt. % of copper, about 8.2 wt. % of iron and about 2.9 wt. % of chromium.
 16. A method as in claim 14 wherein the catalyst is an unsupported catalyst containing about 45.3 wt. % of nickel, about 26.7 wt. % of copper, about 9.9 wt. % of iron and about 3.4 wt. % of chromium.
 17. A method as in claim 14 wherein the catalyst is an unsupported catalyst containing about 30.7 wt. % of nickel, about 12.6 wt. % of copper, about 3.3 wt. % of iron and about 0.64 wt. % of chromium.
 18. A method as in claim 14 wherein the catalyst is an unsupported catalyst containing about 49.1 wt. % of nickel, about 13.9 wt. % of copper, about 17.4 wt. % of iron and about 1.1 wt. % of chromium.
 19. A method as in claim 14 wherein the catalyst is a silica-supported catalyst containing, on an oxygen and silica free basis, about 1 wt. % of nickel, about 0.21 wt. % of copper, about 0.44 wt. % of iron and about 0.1 wt. % of chromium. 